The Synthesis Method of Tin Dioxide Nanoparticles by Plasma-Assisted Electrolysis Process and Gas Sensing Property

Article information

Abstract

1. Introduction

Semiconducting oxide materials such as ZnO₂, In₂O₃, WO₃ and SnO₂ had been investigated to be used as a gas sensor due to its sensitivity to reducing or oxidizing gases. Among these materials, n-type semiconducting material SnO₂ has been intensively studied owing to its high chemical stability on gas sensing condition and electron mobility [1]. Thus, there had been many researches about gas sensing property of SnO₂ with wide range of toxic gases such as ethanol and hydrogen sulfide [2-6]. Due to its characteristic of wide band gap 3.6 eV, it also can be used as transparent conducting oxides (TCOs) [7], optical electronic devise [8] and lithium batteries [9].

SnO₂ gas sensors were usually prepared by way of thick and thin film on the substrate. Thin films are in great interest due to the efficient power consumption and high sensitivity. Nevertheless, it has poor mechanical property and low stability [10]. To enhance this disadvantage, thick films were prepared with the SnO₂ nanoparticles.

The grain boundaries in the polycrystalline metal oxide nanoparticle can trap the charge between the adjacent grains which effected by the Schottky potential barrier [5, 11]. If the tin oxide nanoparticle is exposed to the air ambient, the oxygen adsorbed on the grain boundaries of the particle surface forms O₂^-, O^- and O_2- ions. As a result, it captures the free electrons from the oxygen vacancy, increasing the resistivity. When the reduction gas flows above the metal oxide such as carbon monoxide and ethanol, carbon dioxide and water vapor are produced due to the reaction between the oxygen ions and the reduction gas. It contributes to decrease the resistivity of a metal oxide by releasing the free electrons from the adsorbed O₂^-, O^- and O_2- ions [6]. By detecting these changes, the metal oxide can be used as a gas sensor.

SnO₂ nanoparticles are usually synthesized by precipitation [12], sol-gel [13], hydrothermal [14] and hydrolysis [15]. But these methods use chloride precursors, ammonia or hydroxide solutions to adjust pH and to form hydroxide nanoparticles. Thus, particle size and distribution is sensitive to the pH, using large amount of base solution and spend much time while reacting. To enhance these disadvantages, the plasma-assisted electrolysis process is adapted. Originally, this process is a method of converting metal surface into micro scale thickness oxide layer which is easily corroded in the air ambient such as aluminum, magnesium and titanium [16]. By controlling the conditions of the reaction, metal oxide nanoparticles can be produced instead of forming layers on the metal surface. The arc plasma forms when the current flow is limited by produced gases on the surface of the electrode. Nevertheless, some parts of the electrode are steel contacted with the electrolyte and due to increased current density, the local evaporating is continuously caused. Then, the formed gases envelop the electrode and lower the electrical conductivity. In this region, the electric field strength is enough to ionize the vapor in the gas envelop (10⁶ ~ 10⁸ V/m). Initially, sparks are rapidly formed in gas bubbles and transform into uniform glow by the vapor envelop. The hydrodynamic in this region is stabilized and drops the current density, causing the transformation of glow into intensive arc plasma [17]. As a result, the metal oxide is produced.

This paper focuses on controlling the particle size of a synthesized nano-sized particles and narrowing size distribution to use as a gas sensor by applying the plasmaassisted electrolysis process. Therefore, the concentration of electrolyte and frequency of the voltage condition was controlled. This process is a simple process that can reduce the environmental pollution by using small amount of electrolyte, the reaction time and continuous reaction is possible with the same electrolyte solution.

2. Experimental

2.1. Preparation of tin oxide nanoparticles

Tin metal plate was cut into piece (10 mm × 8 mm), put into the solution consist of D.I water with sulfuric acid electrolyte that can be seen in Fig. 1. The tin metal was put on an anode, a stainless steel mesh was connected to a cathode. The AC power supply (ACP-3KVA, Unicorn TMI Co.) was connected to the two electrodes. The stainless steel mesh (SUS 304, 60 mesh, The Nilaco Co.) was used to supply current equally to whole metal surface. Once the discharges were constantly produced after initial ignition, the condition was kept while proceeding reaction. Due to its high termperature and pressure during reaction, reactor was connected to the chiller (Haake SC 100, Thermo Scientific Co.) to control the solution temperature at 20°C effectively by cycling the solution with pump. Every reaction was finished within 5 minutes due to the quick reaction rate. Synthesized powder was gathered by centrifuge at 10,000 rpm. The powder was washed with an ultrasonic vibrator in DI water for 5 times to remove the electrolyte from the powder. The washed powder was calcinated at 600°C for 2 hours [18].

Fig. 1

Schematic diagram of plasma-assisted electrolysis process.

3. Results and discussion

3.2. Effect of electrolyte concentration

Fig. 2 and 3 shows the morphology and the XRD peak of tin dioxide nanoparticle with the different electrolyte concentration by 5, 7 and 10 mM of sulfuric acid under the voltage of 500 V, 100 Hz. The peak showed almost amorphous state due to the physically adsorbed and chemically bonded water molecules [21]. When the concentration of the electrolyte changed by 5, 7 and 10 mM, the particles size decreased from 100 to 52 nm. When the electrolyte concentration which is sulfuric acid increases, acidity of the solution decreases that is related to the ratio of proton and cations. The Sn ions melted down from the plate should react with cations in solution such as O_2- to form nanoparticles however, lower acidity indicates the lower degree of cations. As a result, it restricts the formation of nanoparticles and reduces nanoparticles size by increasing electrolyte concentration. For the maximization of gas sensing property, 10 mM electrolyte concen- tration condition was fixed for further analysis.

Fig. 2

FE-SEM images of tin dioxide nanoparticle synthesized by plasma-assisted electrolysis process with sulfuric acid electrolyte, (a) 5mM, (b) 7 mM, and (c) 10mM.

Fig. 3

XRD patterns of tin dioxide nanoparticle by changing the mole of electrolyte (a) 5 mM (b) 7 mM (c) 10 mM.

3.3. Effect of voltage frequency

Fig. 4 shows the morphology of the tin dioxide nanoparticle with the different value of frequency by 50, 100, 200 Hz of the power supply in a condition of 500 V. When the frequency increased, the particle size increased from 40 to 76 nm. If the frequency increases, the number of spot where the plasma forms on the metal surface also increases. It contributes the metal to melt continuously without enough time for cooling. Therefore, it could not give sufficient time to form nanoparticle by continuous formation of plasma, resulting in an agglomeration, forming large particles [22]. To be used as gas sensor with large surface area, smallest nanoparticle synthesis condition which is 50 Hz was chosen for optimum state.

Fig. 4

FE-SEM images of tin dioxide nanoparticle by changing the frequency (a) 50Hz (b) 100Hz (c) 200Hz.

3.3. Effect of calcination

Fig. 5 and 6 shows XRD peak of synthesized tin oxide nanoparticle and the peak after calcination of 600°C. Synthesized tin oxide nanoparticle showed almost amorphous state without specific peaks. But after the calcination, the peaks perfectly match with JCPDS card no. 41- 1445 which indicates structure of tetragonal phase tin oxide with (110), (101) and (210) respectively. At higher temperature of calcination, the XRD peak became sharper. It indicates that grain size and the crystallinity can be controlled by calcination temperature.

Fig. 5

XRD patterns of nanoparticle (a) after calcination at 600°C and (b) before calcination.

Fig. 6

FE-SEM images of synthesized nanoparticle calcinated at 10 mM sulfuric acid (a) before calcination and (b) after calcination at 600°C.

3.4. TEM analysis

Fig. 7(a) shows the HR-TEM images of resulting tin dioxide nanoparticles synthesized using plasma-assisted electrolysis process with the size of 40 nm at the condition of 10 mM of sulfuric acid electrolyte, 500 V and 50 Hz. It matches with the SEM analysis of the above results that the spherical morphology nanoparticles are well developed with the narrow size distribution. Fig. 7 (b) shows the surface of the single nanoparticle with the distance between the lattice fringe shows value of 0.33 and 0.26 nm corresponding to the spacing of tetragonal tin dioxide by direction of (110) and (101) respectively. Fig. 7 (c) shows the Fast Fourier transform (FFT) pattern. The bright ring of the pattern indicates each ring is consist of (110), (101), (211) directions. It matches with the polycrystalline nature of nanostructure tin dioxide particle as can be seen in Fig. 7 (b).

Fig. 7

TEM images of tin dioxide powder (a) as-prepared nanoparticle at low resolution (b) at high resolution (c) FFT pattern.

3.5. Gas sensing property

The condition of synthesizing tin dioxide nanoparticle was 500 V, 10 mM of sulfuric acid and 50 Hz for 5 minutes due to the smaller size of the whole condition to increase the specific surface area. The sensing performed at 5 V and the temperature of 350°C. The determination of sensing response was plotted as a ratio of R_a/R_g, where the R_a is the steady-state initial resistance and Rg is the resistance of air-gas mixture in air ambient [23]. Fig. 8 shows the property of as-prepared tin dioxide nanoparticle- based gas sensor of hydrogen sulfide. The flow rate of the gas was 50, 250 and 500 ppm. The response and recovery times were shorten through increasing gas flow rate with 30 and 23, 15 and 25, 12 and 21 s respectively. The time was determined by returning to the 90% of its initial resistance T_90%. When the gas flows, it reacts with the oxygen ions adsorbed on the grain boundaries on the tin dioxide nanoparticle, eliminating oxygen ions. It releases the free electrons into the particle grain boundaries which were captured by the oxygen ions. As a result, the resistance decreases. When the gas was turned off, the oxygen again adsorbs on the metal surface forming oxygen ions. It caused the resistance to be increased. When the gas flow rate increases by 50, 250 and 500 ppm, the sensor sensitivity also increased.

Fig. 8

Sensing properties of as-prepared tin dioxide gas sensor with sensor response and gas flow rate.

4. Conclusion

Tin dioxide nanoparticle could be obtained by using newly process of plasma-assisted electrolysis. By controlling the condition of the reaction such as electrolyte concentration and frequency of the voltage, the particle size could be controlled from 100 to 40 nm. The condition of synthesizing nanoparticles was chosen to be the smallest nanoparticles to be used as a gas sensor which was 500 V and 50 Hz. After the reaction, the synthesized particle was calcinated at 600°C for 2 hours to evaporate the bonded water molecules and increase the crystallinity. This powder was mixed with terpineol to produce paste, put on a glass and calcinated at 500°C for 2 hours to decompose the terpineol, producing tin dioxide nanoparticle-based gas sensor. The gas sensing performed at the temperature of 350°C with hydrogen sulfide gas. It showed potential application as detecting characteristic with enhancing sensitivity when the flow rate of gas increased. By investigating the new environmental friendly process of synthesizing nanoparticles, it has shown great potential in industrial applications.

Article information Continued