- The Selective Leaching of Al-Ni Alloy Nano Powders Prepared by Electrical Wire Explosion
-
Je-Shin Park, Won-Baek Kim, Chang-Youl Suh, Han-Kwon Chang, Jong-Gwan Ahn, Byoung-Kyu Kim
-
J Korean Powder Metall Inst. 2008;15(4):308-313.
-
DOI: https://doi.org/10.4150/KPMI.2008.15.4.308
-
-
 Abstract
 PDF
- Al-Ni alloy nano powders have been produced by the electrical explosion of Ni-plated Al wire. The porous nano particles were prepared by leaching for Al-Ni alloy nano powders in 20wt% NaOH aqueous solution. The structural properties of leached porous nano powder were investigated by nitrogen physisorption, X-ray diffraction (XRD) and transmission Microscope (TEM). The surface areas of the leached powders were increased with amounts of AI in alloys. The pore size distributions of these powders were exhibited maxima at range of pore diameters 3.0 to 3.5 nm from the desorption isotherm. The maximum values of those were decreased with amounts of Al in alloys.
- Fabrication of Porous Nano Particles from Al-Cu Alloy Nano Powders Prepared by Electrical Wire Explosion
-
Je-Shin Park, Won-Baek Kim, Chang-Youl Suh, Jong-Gwan Ahn, Byoung-Kyu Kim
-
J Korean Powder Metall Inst. 2008;15(3):234-238.
-
DOI: https://doi.org/10.4150/KPMI.2008.15.3.234
-
-
150
View
-
0
Download
-
2
Citations
-
Abstract
PDF
- Al-Cu alloy nano powders have been produced by the electrical explosion of Cu-plated Al wire. The porous nano particles were prepared by leaching for Al-Cu alloy nano powders in 40wt% NaOH aqueous solution. The surface area of leached powder for 5 hours was 4 times larger than that of original alloy nano powder. It is demonstrated that porous nano particles could be obtained by selective leaching of alloy nano powder. It is expected that porous Cu nano powders can be applied for catalyst of SRM (steam reforming methanol).
-
Citations
Citations to this article as recorded by  - Fabrication of Ni-free Fe-based Alloy Nano Powder by Pulsed Wire Evaporation in Liquid: Part 2. Effect of Solvent and Comparison of Fabricated Powder owing to Fabrication Method
Ho-Jin Ryu, Yong-Heui Lee, Kwang-Ug Son, Young-Min Kong, Jin-Chun Kim, Byoung-Kee Kim, Jung-Yeul Yun
Journal of Korean Powder Metallurgy Institute.2011; 18(2): 112. CrossRef - Fabrication of Ni-free Fe-based Alloy Nano Powder by Pulsed Wire Evaporation in Liquid: Part I. Effect of Wire Diameter and Applied Voltage
Ho-Jin Ryu, Yong-Heui Lee, Kwang-Ug Son, Young-Min Kong, Jin-Chun Kim, Byoung-Kee Kim, Jung-Yeul Yun
Journal of Korean Powder Metallurgy Institute.2011; 18(2): 105. CrossRef
|
kpmi