- Characterization and Stability of Silver Nanoparticles in Aqueous Solutions
-
L.H. Bac, W.H. Gu, J.C. Kim, B.K. Kim, J.S. Kim
-
J Korean Powder Metall Inst. 2012;19(1):55-59.
-
DOI: https://doi.org/10.4150/KPMI.2012.19.1.055
-
-
244
View
-
0
Download
-
4
Citations
-
 Abstract
 PDF
- In this work, the silver nanoparticles have been synthesized by electrical explosion of wire in three liquid mediums: deionized water (DIW), polyvinylpyrrolidone (PVP) and sodium dodecyl benzene sulfonate (SDBS) solutions. Absorption in the UV-visible region of these suspensions was measured in the range of 300-800 nm. A surface plasmon peak was observed at ~400 nm in all suspensions in measured wavelength range. Particle size was analyzed by transmission electron microscope. It showed that the particles had nearly spherical shape in all samples. The average particle sizes prepared in DIW, PVP and SDBS solution were 37, 31 and 27 nm, respectively. Stability of the suspensions was estimated by multiple light scattering method. The presence of PVP and SDBS surfactants in the exploding medium resulted in enhanced stability of the silver suspensions.
-
Citations
Citations to this article as recorded by  - Plasma-chemical Synthesis of Silver Nanoparticles in the Presence of Citrate
Margarita Skіba, Alexander Pivovarov, Anna Makarova, Victoria Vorobyova
Chemistry Journal of Moldova.2018; 13(1): 7. CrossRef - Fabrication and Characterization of Ag Particles by Polyol Process and Wet Chemical Process
Juyeon Yoo, Hyosung Jang, Kun-Jae Lee
Journal of Korean Powder Metallurgy Institute.2016; 23(4): 297. CrossRef - A Study of the Preparation and Properties of Antioxidative Copper Inks with High Electrical Conductivity
Chia-Yang Tsai, Wei-Chen Chang, Guan-Lin Chen, Cheng-Huan Chung, Jun-Xiang Liang, Wei-Yang Ma, Tsun-Neng Yang
Nanoscale Research Letters.2015;[Epub] CrossRef - Fabrication of Micro Pattern on Flexible Substrate by Nano Ink using Superhydrophobic Effect
Soo-Jung Son, Young-Sang Cho, Jong Joo Rha, Chul-Jin Cho
Journal of Korean Powder Metallurgy Institute.2013; 20(2): 120. CrossRef
|
kpmi