Microstructural examination of the Nb-Si-B alloys at Nb-rich compositions is performed. The Nb-rich corner of the Nb-Si-B system is favorable in that the constituent phases are Nb (ductile and tough phase with high melting temperature) and T₂ phase (very hard intermetallic compound with favorable oxidation resistance) which are good combination for high temperature structural materials. The samples containing compositions near Nb-rich corner of the Nb- Si-B ternary system are prepared by spark plasma sintering (SPS) process using T₂ and Nb powders. T₂ bulk phase is made in arc furnace by melting the Nb slug and the Si-B powder compact. The T₂ bulk phase was subsequently ballmilled to powders. SPS is performed at 1300°C and 1400°C, depending on the composition, under 30 MPa for 600s, to produce disc-shaped specimen with 15 mm in diameter and 3 mm high. Hardness tests (Rockwell A-scale and micro Vickers) are carried out to estimate the mechanical property.

Citations

Citations to this article as recorded by  

• Fabrication of Nb-Si-B Alloys Using the Pulverized Nb-T₂ Alloy Powder
  Min-Ho Cho, Sung-Jun Kim, Hyun-Ji Kang, Sung-Tag Oh, Young Do Kim, Seong Lee, Myung Jin Suk
  Journal of Korean Powder Metallurgy Institute.2019; 26(4): 299.     CrossRef
• Mechanical properties of Mo-Nb-Si-B quaternary alloy fabricated by powder metallurgical method
  Jong Min Byun, Su-Ryong Bang, Se Hoon Kim, Won June Choi, Young Do Kim
  International Journal of Refractory Metals and Hard Materials.2017; 65: 14.     CrossRef
• Mechanical properties of Mo-Si-B alloys fabricated by using core-shell powder with dispersion of yttria nanoparticles
  Jong Min Byun, Su-Ryong Bang, Won June Choi, Min Sang Kim, Goo Won Noh, Young Do Kim
  Metals and Materials International.2017; 23(1): 170.     CrossRef
• Fabrication of Ta2O5 Dispersion-Strengthened Mo-Si-B Alloy by Powder Metallurgical Method
  Jong Min Byun, Won June Choi, Su-Ryong Bang, Chun Woong Park, Young Do Kim
  JOM.2017; 69(4): 683.     CrossRef
• Rapid consolidation of nanostuctured WC-FeAl3 by pulsed current activated heating and its mechanical properties
  In-Jin Shon, Seok-Jae Lee
  International Journal of Refractory Metals and Hard Materials.2017; 65: 69.     CrossRef