A powder-in-sheath rolling method was applied to a fabrication of a carbon nano tube (CNT) reinforced aluminum composite. A STS304 tube with an outer diameter of 34 mm and a wall thickness of 2 mm was used as a sheath material. A mixture of pure aluminum powders and CNTs with the volume contents of 1, 3, 5 vol was filled in the tube by tap filling and then processed to 73.5% height reduction by a rolling mill. The relative density of the CNT/ Al composite fabricated by the powder-in-sheath rolling decreased slightly with increasing of CNTs content, but exhibited high value more than 98. The grain size of the aluminum matrix was largely decreased with addition of CNTs; it decreased from 24 μm to 0.9 μm by the addition of only 1 volCNT. The average hardness of the composites increased by approximately 3 times with the addition of CNTs, comparing to that of unreinforced pure aluminum. It is concluded that the powder-in-sheath rolling method is an effective process for fabrication of CNT reinforced Al matrix composites.

Citations

Citations to this article as recorded by  

• Torsion Property of the Structure Bonded Aluminum Foam Due to Impact
  G.W. Hwang, J.U. Cho
  Archives of Metallurgy and Materials.2017; 62(2): 1353.     CrossRef
• A Fatigue Fracture Study on TDCB Aluminum Foam Specimen of Type Mode III Bonded with Adhesive
  J.H. Lee, J.U. Cho
  Archives of Metallurgy and Materials.2017; 62(2): 1359.     CrossRef
• Experimental Study On Fracture Property Of Double Cantilever Beam Specimen With Aluminum Foam
  Y.C. Kim, H.K. Choi, J.U. Cho
  Archives of Metallurgy and Materials.2015; 60(2): 1151.     CrossRef
• Experimental Study On Fracture Property Of Tapered Double Cantilever Beam Specimen With Aluminum Foam
  Y.C. Kim, S.S. Kim, J.U. Cho
  Archives of Metallurgy and Materials.2015; 60(2): 1459.     CrossRef
• Microstructure and Mechanical Properties of CNT/Al Composite Fabricated by a Powder-in-Sheath Rolling Method utilizing Copper Tube as a Sheath
  Seong-Hee Lee
  Journal of Korean Powder Metallurgy Institute.2014; 21(5): 343.     CrossRef