A lean alloy is defined as a low alloy steel that minimizes the content of the alloying elements, while maintaining the characteristics of the sintered alloy. The purpose of this study is to determine the change in microstructure and mechanical properties due to the addition of silicon or tin in Fe-Mo-P, Fe-Mn-P, and Fe-Mo-Mn-P alloys. Silicon- or tin-added F-Mo-P, Fe-Mn-P, and Fe-Mo-Mn-P master alloys were compacted at 700 MPa and subsequently sintered under a H₂-N₂ atmosphere at 1120°C. The sintered density of three alloy systems decreases under the same compacting pressure due to dimensional expansion with increasing Si content. As the diffusion rate in the Fe-P-Mo system is higher than that in the Fe-P-Mn system, the decrease in the sintered density is the largest in the Fe-PMn system. The sintered density of Sn added alloys does not change with the increasing Sn content due to the effect of non-dimensional changes. However, the effect of Si addition on the transverse rupture strengthening enhancement is stronger than that of Sn addition in these lean alloys.

A lean alloy is defined as a low alloy steel with a minimum amount of the alloying element that maintains the characteristics of the sintered alloy. It is well known that the addition of elements such as Cr, P, Si, or Mn improves the mechanical characteristics of the alloy, but decreases the sinterability. The mother alloy is used to avoid an oxidation reaction with the alloying elements of Cr, P, Si or Mn. The purpose of this study is to determine the change in the mechanical properties of Fe-P-Mo and Fe-P-Mn alloys as a result of the addition of Si. In this article, the Fe-P-Mo and Fe-P-Mn alloys to which Si is added are compacted at 7.0 g/cm³ and then sintered in H₂-N₂ at 1120°C. The P around the macropores and large grains reduces due to the formation of SiO₂ as the Si content increases. This is caused by the increase in strength owing to reducing intergranular fracture by suppressing the reaction with oxygen.

Citations

Citations to this article as recorded by  

• The Effects of Si or Sn on the Sintered Properties of Fe-(Mo,Mn)-P Lean alloy
  Woo-Young Jung, Jin-Uk Ok, Dong-Kyu Park, In-Shup Ahn
  Journal of Korean Powder Metallurgy Institute.2018; 25(4): 302.     CrossRef
• Sintering behavior of Fe-(Mo-Mn-P)-xSi alloys according to the Green Density
  Woo-Young Jung, Jin-Uk Ok, Dong-Kyu Park, In-Shup Ahn
  Journal of Korean Powder Metallurgy Institute.2017; 24(5): 400.     CrossRef