Abstract

MoSi_2-TiC composite powders were fabricated by in-situ reaction through mechanical alloying. Also the monolithic MoSi_2 as well as TiC were synthesiced by mechanical alloying for comparison. An abrupt increase of vial surface temperature was detected due to a sudden reaction between elemental powders during milling. The reaction time for synthesis of composite powders decreased with increasing the content of (Ti+C) powder. It was found that a significant decrease of Ti grain size was observed with increasing the milling time. And the synthesis reaction of MoSi_2-TiC composite powders were largely dependent on the reaction between Ti and C powders.