- HOME > J Korean Powder Metall Inst > Volume 12(5); 2005 > Article
- 전기방전소결에 의해 제조된 다공성 및 다공성 표면을 갖는 Ti-6Al-4V 임플란트 : (2) 경도 및 압축강도
- 현창용, 허재근, 이원희
- Porous and Porous Surfaced Ti-6Al-4V Implants Fabricated by Electro-Discharge-Sintering : (2) Hardness and Compressive Strength
- C. Y. Hyun, J. K. Huh, W. H. Lee
-
Journal of Korean Powder Metallurgy Institute 2005;12(5):332-335
DOI: https://doi.org/10.4150/KPMI.2005.12.5.332
2서울산업대학교 신소재공학과
3세종대학교 신소재공학과
1Department of Materials Engineering, Seoul National University of Technology
2Department of Materials Engineering, Seoul National University of Technology
3Department of Advanced Materials Engineering, Sejong University
- 10 Views
- 0 Download
- 0 Crossref
- 0 Scopus
Abstract
Porous and porous surfaced Ti-6Al-4V implant compacts were fabricated by electro-discharge-sintering (EDS) of atomized spherical Ti-6Al-4V powders with a diameter of 100-150;µm, The solid core formed in the center of the compact after discharge was composed of acicular alpha+beta Widmanstatten grains, The hardness value at the solid core was much higher than that at the particle interface or particles in the porous layer, which can be attributed to both heat treatment and work hardening effects induced from EDS, The compressive yield strength was in a range of 19 to 436 MPa which significantly depends on both input energy and capacitance, Selected porous-surfaced Ti-6Al-4V implant compacts with a solid core have much higher compressive strengths compared to the human teeth and sintered Ti dental implants.
Cited- Related articles
-