This study investigates the oxidation properties of Fe-14Cr ferritic oxide-dispersion-strengthened (ODS) steel at various high temperatures (900, 1000, and 1100°C for 24 h). The initial microstructure shows that no clear structural change occurs even under high-temperature heat treatment, and the average measured grain size is 0.4 and 1.1 μm for the as-fabricated and heat-treated specimens, respectively. Y–Ti–O nanoclusters 10–50 nm in size are observed. High-temperature oxidation results show that the weight increases by 0.27 and 0.29 mg/cm² for the asfabricated and heat-treated (900°C) specimens, and by 0.47 and 0.50 mg/cm² for the as-fabricated and heat-treated (1000°C) specimens, respectively. Further, after 24 h oxidation tests, the weight increases by 56.50 and 100.60 mg/cm² for the as-fabricated and heat-treated (1100°C) specimens, respectively; the latter increase is approximately 100 times higher than that at 1000°C. Observation of the surface after the oxidation test shows that Cr₂O₃ is the main oxide on a specimen tested at 1000°C, whereas Fe₂O₃ and Fe₃O₄ phases also form on a specimen tested at 1100°C, where the weight increases rapidly. The high-temperature oxidation behavior of Fe-14Cr ODS steel is confirmed to be dominated by changes in the Cr₂O₃ layer and generation of Fe-based oxides through evaporation.

Citations

Citations to this article as recorded by  

• Microstructure and Wear Properties of Oxide Dispersion Strengthened Steel Powder Added Steel-Based Composite Material for Automotive Part
  Young-Kyun Kim, Jong-Kwan Park, Kee-Ahn Lee
  journal of Korean Powder Metallurgy Institute.2018; 25(1): 36.     CrossRef