Cobalt coated tungsten carbide-cobalt composite powder has been prepared through wet chemical reduction method. The cobalt sulfate solution was converted to the cobalt chloride then the cobalt hydroxide. The tungsten carbide powders were added in to the cobalt hydroxide, the cobalt hydroxide was reduced and coated over tungsten carbide powder using hypo-phosphorous acid. Both the cobalt and the tungsten carbide phase peaks were evident in the tungsten carbide-cobalt composite powder by X-ray diffraction. The average particle size measured via scanning electron microscope, particle size analysis was around 380 nm and the thickness of coated cobalt was determined to be 30~40 nm by transmission electron microscopy.

Citations

Citations to this article as recorded by  

• Electroless Ni-P deposition on WC powders through direct PdCl2 activation and study on the underlying mechanisms
  Peng Tang, Shuwen Jiang, Jiawei Yan, Xianquan Li
  Next Materials.2025; 6: 100496.     CrossRef
• Pre-treatments of initial materials for controlling synthesized TaC characteristics in the SHS process
  Jae Jin Sim, Sang Hoon Choi, Ji Hwan Park, Il Kyu Park, Jae Hong Lim, Kyoung Tae Park
  journal of Korean Powder Metallurgy Institute.2018; 25(3): 251.     CrossRef
• Spark plasma sintering of WC–Co tool materials prepared with emphasis on WC core–Co shell structure development
  Sungkyu Lee, Hyun Seon Hong, Hyo-Seob Kim, Soon-Jik Hong, Jin-Ho Yoon
  International Journal of Refractory Metals and Hard Materials.2015; 53: 41.     CrossRef