Composites of P25 TiO₂ and hexagonal WO₃ nanorods are synthesized through ball-milling in order to study photocatalytic properties. Various composites of TiO₂/WO₃ are prepared by controlling the weight percentages (wt%) of WO₃, in the range of 1–30 wt%, and milling time to investigate the effects of the composition ratio on the photocatalytic properties. Scanning electron microscopy, x-ray diffraction, and transmission electron microscopy are performed to characterize the structure, shape and size of the synthesized composites of TiO₂/WO₃. Methylene blue is used as a test dye to analyze the photocatalytic properties of the synthesized composite material. The photocatalytic activity shows that the decomposition efficiency of the dye due to the photocatalytic effect is the highest in the TiO₂/WO₃ (3 wt%) composite, and the catalytic efficiency decreases sharply when the amount of WO₃ is further increased. As the amount of WO₃ added increases, dye-removal by adsorption occurs during centrifugation, instead of the decomposition of dyes by photocatalysts. Finally, TiO₂/WO₃ (3 wt%) composites are synthesized with various milling times. Experimental results show that the milling time has the best catalytic efficiency at 30 min, after which it gradually decreases. There is no significant change after 1 hour.

Transition-metal oxide semiconductors have various band gaps. Therefore, many studies have been conducted in various application fields. Among these, methods for the adsorption of organic dyes and utilization of photocatalytic properties have been developed using various metal oxides. In this study, the adsorption and photocatalytic effects of WO₃ nanomaterials prepared by hydrothermal synthesis are investigated, with citric acid added in the hydrothermal process as a structure-directing agent. The nanostructures of WO₃ are studied using transmission electron microscopy and scanning electron microscopy images. The crystal structure is investigated using X-ray diffraction patterns, and the changes in the dye concentrations adsorbed on WO₃ nanorods are measured with a UV-visible absorption spectrophotometer based on Beer-Lambert’s law. The methylene blue (MB) dye solution is subjected to acid or base conditions to monitor the change in the maximum adsorption amount in relation to the pH. The maximum adsorption capacity is observed at pH 3. In addition to the dye adsorption, UV irradiation is carried out to investigate the decomposition of the MB dye as a result of photocatalytic effects. Significant photocatalytic properties are observed and compared with the adsorption effects for dye removal.

Citations

Citations to this article as recorded by  

• Photocatalytic Properties of WO₃ Thin Films Prepared by Electrodeposition Method
  Kwang-Mo Kang, Ji-Hye Jeong, Ga-In Lee, Jae-Min Im, Hyun-Jeong Cheon, Deok-Hyeon Kim, Yoon-Chae Nah
  Journal of Korean Powder Metallurgy Institute.2019; 26(1): 40.     CrossRef
• Photocatalysis of TiO₂/WO₃ Composites Synthesized by Ball Milling
  Su-Yeol Yu, Chunghee Nam
  Journal of Korean Powder Metallurgy Institute.2018; 25(4): 316.     CrossRef